A theoretical insight into the fracture behavior of the edge-cracked polycrystalline BC3 nanosheets

A Dadrasi and S Fooladpanjeh and A Albooyeh and A Salmankhani and AH Mashhadzadeh and MR Saeb, COMPUTATIONAL MATERIALS SCIENCE, 192, 110345 (2021).

DOI: 10.1016/j.commatsci.2021.110345

This work aims to investigate the mechanical and fracture behavior of mono- and polycrystalline BC3 nanosheets (MC- and PCBC3NS) in terms of the number of grain boundaries, status of edge-cracks, and temperature. By using molecular dynamics simulation, appropriate potential function and boundary conditions, MC- and PCBC3NS were modeled and tested varying the temperature and crack length. Results demonstrated that the mechanical properties of MCBC(3)NSs were decreased as the temperature or the crack length increased, where higher properties were achieved in the armchair direction. Stress intensity variation followed a similar trend upon temperature, but increased as the crack length increased. The minimal elastic modulus, failure stress, and failure strain of the MCBC3NS, for crack length L/2, zigzag direction, and at 1000 K were respectively 53%, 84%, and 75% lower compated to values at 100 K. The same trend was detected for PCBC(3)NSs upon crack length increase at 300 K, while the properties of PCBC(3)NSs were lower than the corresponding MCBC3NS. Moreover, for the PCBC(3)NSs with smaller cracks, both the crack length and grain boundary played key roles in the fracture process, while for large cracked nanosheets the effect of grain boundary was negligible. This work unveiled the fingerprint of the fracture behavior of 2D nanosheets which enlightens future ahead of next generations of nano-devices.

Return to Publications page