SI Konorev and R Kozubski and M Albrecht and IA Vladymyrskyi, COMPUTATIONAL MATERIALS SCIENCE, 192, 110337 (2021).

DOI: 10.1016/j.commatsci.2021.110337

Vacancy-mediated lattice diffusion coefficients of Fe and Pt atoms in the chemically ordered L1(0)-FePt phase at temperatures between 1300 and 1600 K were evaluated by means of Molecular Dynamics (MD) simulations. Due to the anisotropic structure of the L1(0)-ordered FePt phase, Fe and Pt diffusion fluxes and the resulting self diffusion coefficients were considered along and perpendicular to the 001 crystallographic direction. In view of a very low vacancy concentration in real FePt single crystals, steady state conditions of the simulated process were approximated by specifically scaling the self-diffusion coefficients estimated for higher vacancy concentrations to the equilibrium vacancy concentration. This procedure involved the calculation of vacancy formation energies which appeared temperature dependent. The validity of this approach was thoroughly tested and the final results were analyzed and compared to the relevant literature data. The evaluated temperature dependent Fe and Pt self-diffusion coefficients showed Arrhenius behavior, however, their values were much lower than the reported experimental ones. Apart from the inevitable effect of the applied quasi-empirical potentials, the discrepancies might originate from the fact that while the MD simulations addressed a single crystal of FePt defected exclusively with vacancies and antisites, the existence of fast diffusion paths along linear and planar defects cannot be excluded in real materials.

Return to Publications page