Dislocation cross-slip in precipitation hardened Mg-Nd alloys

ZH Huang and CM Yang and JE Allison and L Qi and A Misra, JOURNAL OF ALLOYS AND COMPOUNDS, 859, 157858 (2021).

DOI: 10.1016/j.jallcom.2020.157858

An integrated experimental characterization and molecular dynamics (MD) simulation approach was used to explore the dislocation-precipitate interactions in a dilute Magnesium-Neodymium (Mg-Nd) precipitation hardened alloy. In situ indentation in a transmission electron microscope (TEM) and postmortem TEM characterization of deformed samples and MD simulations revealed that basal type dislocations interacted differently with beta(1) (Mg3Nd) and beta''' (Mg3-7Nd) precipitates. For beta''' precipitates, the basal dislocations directly shear the precipitates. For beta(1) precipitates, such shearing becomes much more difficult because it requires the creation of antiphase boundaries in the ordered lattice of beta(1) precipitates. Screw dislocations were observed to cross-slip from basal to the prismatic plane, which could be parallel to the broad facet of beta(1) precipitates. It is postulated that double cross-slip (basal to prismatic to basal) via the Hirsch mechanism may enable screw dislocations to overcome the beta(1) precipitates. MD simulations also revealed that an edge dislocation is unable to bypass the precipitate via the generation of screw dislocation segments plus the double cross-slip mechanism. The edge dislocation can bow around the precipitate, and the segment that adopts a screw character can cross-slip to the prismatic plane but with increasing applied stress, cross-slips back to the original basal plane to continue glide via precipitate shearing. The implication of glide dislocation - beta(1)-precipitate interaction mechanisms on the strength and ductility of beta(1) precipitate dominant microstructures is discussed. (C) 2020 Elsevier B.V. All rights reserved.

Return to Publications page